High temperature wear-resistant alloy steel is produced by smelting and other processes using the following components and weight percentage of raw materials: 77.5 ~ 79% scrap steel, 18.3 ~ 20 7% high carbon ferrochrome, 0.67 ~ 1.0% ferro molybdenum, 0.33 ~ 0.5% iron vanadium, appropriate amount of silicon, manganese deoxidizer, 0,05 ~ 0,1% Ferrotitanium, 0,02 ~ 0,05% Zirconium, 0,6 ~ 1,2% ya aluminium mpe 0,12 ~ 0,5% ya ba éléments ya mabele ya rare. Ba acier ya alliage oyo esalemi na ndenge wana ezali na 1,45 ~ 1,70% ya carbone, 11,0 ~ 12,5% ya chrome, 0,4 ~ 0,6% molybdène, 0,15 ~ 0,30% Vanadium, 0,02 ~ 0,05% ya titanium, 0,05 0,00 0,0, 1,2% aluminium mpe 0,05 ~ 0,15% ba éléments ya mabele oyo ezali rare.
High temperature wear-resisting alloy steel can significantly change the thermal stability and wear-resisting properties of alloy steel by multi-element and small amount alloying, melt purification, heat treatment strengthening and microstructure refinement, and make the crystal thinning, carbide fine and uniform distribution, but also has excellent comprehensive properties in hardness, tensile strength, impact toughness, thermal erosion rate, friction and wear loss, etc. Therefore, it is the ideal material for manufacturing high temperature Roue de guide et rouleau résistant à l'usure na Industrie ya métallurgie ya fer na acier.
Plaque de doublure à la moulin à boule à l’arrêt Inclus la plaque de base de doublure résistantes à l’usure, plaque de base de plaque de doublure résistantes est disposées sur le haut de la libulu ya fil ya installation, plaque de base ya plaque de doublure oyo ekoki ko délaîter na se ezali fixe connecté na plaque ya réduction ya stress, plaque ya réduction ya stress na se ezali relié na plaque ya renforcement ya makasi, plaque de doublure ya usure ezali na kati ya symème, rainure ezali na likolo, rainure ezali na likolo ya grouove. Efelo ya rainure mokomoko ekangisami na esika moko na likonzí ya amortissement, likoló ya likonzí ya amortissement ekangami na esika moko na caoutchouc, mpe efelo ya libándá ya caoutchouc ezali kogumbama oyo ekangisami na efelo ya kati ya esika oyo ekangami.
Plaque ya doublure ya moulin ya boule ekoki kokitisa makelele oyo esalemi na substrat ya plaque ya doublure oyo ekoki kolata te na processus ya grind ya minerais na nzela ya tableau oyo ezo absorber son, barre ya positionnement, rainure ya installation, plaque ya réduction ya stress, pad ya caoutchouc, absorbeur mpe plaque ya renforcement ya makasi na nzela ya tableau absorbant ya son, mpo na ko éviter bruit oyo esalemi na pollution na esika oyo ezali zinga zinga, mpe ko positionner ba bars. Fréquence ya vibration entre plaque ya doublure oyo ezo résister na usure na moulin ya boule ya mine ekoki ko réduire na caoutchouc, po na ko réduire vibration oyo esalemi na plaque ya doublure résistantes .