CrMnN Furnace Base Plate, na grade standard ya Chine ZG30Cr18Mn12Si2N (GB/T 8492), ezali acier fonte oyo esalemi na ndenge ya lipanda na nickel-kobatela molunge ya austénitique-resistants na Chine. Esalemi mpenza mpo na ntango molai-temperature ya likolo-temperature (950–1050 degrés ), kilo-charge, mpe mbala na mbala kobanda-kotika mosala conditions, esalela manganèse mpe azote mpo na kozwa esika ya nickel ya ntalo, kokokisa performance comparable na likolo-nickel alliages (310S/HP40) ntango kokitisa ba coûts na 30–40%. Ezali solution oyo ezali na talo mingi-efficace mpe ya kozala na confiance mpo na ba fours ya chariot, ba fours ya boîte, ba fours à poutres marches, mpe ba équipements ndenge na ndenge ya traitement ya chaleur.
Composition ya matériel (GB/T 8492, poids%)
C: 0.26–0.36 (Bolendisi ya carbure, bokatikati ya makasi mpe bokasi)
Cr: 17–19 (Esalaka film ya Cr2O3 dense, noyau ya résistance ya oxydation)
Mn: 11–13 (E stabiliser austénite, ebongisaka duresse, e remplacer nickel)
Si: 1.5–2.5 (Ematisaka résistance ya oxydation mpe résistance ya carburisation)
N: 0.2–0.3 (Bokasi ya solution solide, résistance na creep, bopeto ya mbuma)
P/S: Moke to ekokani na 0,04 (Bosoto ya nse, kobongisa stabilité ya température ya likolo-)
Equivalent ya mokili mobimba: Note oyo ekokani na yango mpenza te; mpo na exportation, ekoki kozala na marque lokola "Equivalent to DIN G-X30CrMnSiN18-12-2 / Custom ASTM A743" na ba rapports ya composition chimique mpe propriété mécanique.
Avantages ya moboko
✅ Résistance ya température ya likolo, Résistance ya creep & Long-Term Non-Deformation
Température ya mosala ya ntango molai-: 950–1050 degré ; température ya sommet ya tango mokuse-: 1200 degrés . Force ya rupture ya creep na 1000 degrés Monene to ekokani na 45MPa/1000h, résistance ya creep excellent. Coefficient ya expansion thermique ezali kaka 14,5×10−6/ degré , déformation thermique minimale. Esilisaka point ya mpasi ya industrie : fer fonte/acier carbone ordinaire e déformer na 6 mois, alors que CrMnN ekoki kosalelama pendant 3–5 ans.
✅ Résistance makasi na oxydation, Échelle te & Slagging te
Bobungisi ya oxydation na 1000 degrés < 0,1%/1000h. Film oxyde composite ya Cr2O3+SiO2, résistants na oxydation na corrosion ya soufre. Ezali koboya ete écaille ya oxyde ekita mpo na kobebisa biloko ya mosala, kobongisa bopɛto ya biloko.
✅ Résistance na choc thermique, Résistance na fatigue & Pas de fissure
Pete te mpo na kopasuka na nse ya malili mpe molunge ya mbangu mbala na mbala (Δt > 800 degrés ). Coulée intégrale + conception ya côte renforcement, ba coutures ya soudure te to splicing te, kosilisa ba fissures ya soudure. Bomoi ya bolembi ya molunge ezali mbala 2–3 koleka biloko ya bonkoko.
✅ Duresse ya likolo, Résistance ya kolata & Charge makasi-Capacité ya roulement
Duresse jusqu'à HV500+ (≈HRC50), résistance ya kolata malamu koleka acier ya manganèse ya likolo. Charge ya température ya likolo-makoki ya kosimba: 6–10 t/m2, kokokisa bamposa ya traitement ya chaleur ya pièce de travail ya kilo.
✅ Nickel-Kobomba & Ntalo-Ezali malamu
Design sans nickel-, talo ya 30–40% na se koleka 310S/HP40. Bomoi ya mosala molai, bobateli moke, mpe bobungisi ya bokangami moke, kokokisa motuya ya cycle ya bomoi mobimba ya malamu.
Ba scénarios ya application ya momesano
Mitindo ya ba fours oyo ebongi: Ba fours ya traitement ya chaleur ya chariot, ba fours ya résistance ya boîte, ba fours à poutres marches, ba fours ya chauffage, ba fours ya recuit, ba fours ya extinction.
Ba Industries oyo ekoki kosalelama: Métalurgie, ba pièces ya mituka, fabrication ya ba machines, forge, ba usines ya traitement chaleur.
Bokokani ya ezalela ya mosala: Température: 850–1100 degrés ; Atmosphère: Mopɛpɛ, oyo ekómisaka oxydation, oyo ezali na eloko te, oyo ekitisaka na bolɛmbu; Charge: Charge ya kilo, kokota mpe kobima mbala na mbala, ko chauffer mpe ko refroidir périodique.
Processus ya fabrication (Ezali ko déterminer vie ya service) .
Batching ya bopeto ya likolo- + fondue ya précision (1580–1620 degré ) .
Coulée intégrale ya mousse ebunga (moulage moko-pièce, coutures ya soudure te, taille précise)
Traitement chaleur ya solution (clé: ko stabiliser structure, ko éliminer stress, ko améliorer duresse)
Kosilisa + kosala na masini + komeka oyo ebebisaka te (UT/MT) .
Inspection dimensionnelle + rapport ya matériel + certificat ya usine
Caractéristiques structurelles: Plaque épaisse + mikuwa ya renforcement coulée intégrale; ezali na ba types ya plaque plat, bande, grille, porous respiration; entièrement personnalisable selon ba dessins.
Spécifications & Personnalisation ya makambo
Bolai: 20–50 mm; Bolai: 1000–1250 mm; Bolai: 6000–6500 mm; Bokeli: Plaque plat, mikuwa ya renforcement, porous, forme spécial-; Livraison: Personnalisé selon dessins, livraison rapide, garantie ya 12 mois.
Service ya exportation: Kopesa certificat ya matériel, rapport ya propriété mécanique, rapport ya test non-destructif, English COC, kosunga livraison mondiale.
Pourquoi Pona Plaque Ya Base Ya Fourn CrMnN Na biso?
✔ Original Factory Casting: Contrôle ya processus mobimba-, ba intermédiaires te
✔ Matériel stable: Kotosa mpenza GB/T 8492, composition uniforme mpe performance constante
✔ Processus ya précision: Mousse oyo ebunga + traitement ya chaleur ya solution, vie ya service 30%+ eleki ba usines ordinaires
✔ Non-Personnalisation standard: Taille/structure nionso ekoki kobimisama
✔ Expérience ya exportation: Biloko oyo e exporter na UE, Sud-Est ya Asie, Moyen-Orient, Afrique, na lokumu malamu
✔ Lisungi ya tekiniki: Toli ya kopona ya ofele mpe ba solutions ya adaptation ya condition ya mosala
Maloba ya nsuka
Plaque de base ya four CrMnN (ZG30Cr18Mn12Si2N) ezali solution ya charge-ya malamu pona ba fours ya traitement ya chaleur ya température ya likolo-. Ezali na stabilité ya tango molayi-na 1050 degrés , résistance na déformation, résistance na fissure, résistance na oxydation, économie ya coût ya 30–40% na ko remplacer ba alliages ya nickel ya likolo-, coulée intégrale na vie ya service ya 3–5 ans, mpe ba normes mondiales pona exportation. Tika production mpo na remplacement ya plaque ya base ya four mbala na mbala! Pona CrMnN mpo na investissement ya mbala moko-, stabilité ya tango molayi-, kokitisa ba coûts mpe kobongisa efficacité.
Bokutana na Biso